MainComposition | Oxygen conten% | Fisher size | Typical laser | Apparent density,μm | Theoretical density |
|
| g/cm3 |
FeCoCu | <0.8 | 1.5-4.5 | 10-20 | 1.1-1.7 | 8.36 |
FeCo | <0.8 | 2-5 | 15-25 | 1.1-1.7 | 8.01 |
FeCoCu | <0.8 | 3-6 | 15-25 | 1.1-1.7 | 8.18 |
FeCoCu | <0.8 | 2-5 | 10-20 | 1.1-1.7 | 8.62 |
FeCoCu | <0.8 | 2-5 | 10-20 | 1.1-1.7 | 8.75 |
FeCoCu | <0.8 | 3-6 | 15-25 | 1.1-1.7 | 8.02 |
FeCo | <0.8 | 2-4 | 15-20 | 1.1-1.7 | 8.4 |
FeCoCu | <0.8 | 2-4 | 15-20 | 1.1-1.7 | 8.08 |
FeCoCu | <0.8 | 2-4 | 10-15 | 1.1-1.7 | 8.16 |
FeCoCu | <0.8 | 2-5 | 15-25 | 1.1-1.7 | 8.43 |
CoNi | <0.8 | 0.8-2.0 | 13-23 | 0.5-1.8 | 8.9 |
CoMn | <1.0 | 1.5-3.0 | 15-25 | 1.0-2.5 | 8.9 |
FeCoCu | <0.8 | 2-4 | 10-20 | 0.9-1.6 | 8.37 |
Feature
Porous agglomerate powder, average particle size diameter 8-20μm, high specific surface area, high activity of powder,
and gaining high sintering hardness at relatively low sintering temperature.
Used in non-pressure sintering and laser blade carcass material,diamond saw blades, laser welding and other diamond tools.
With high ductility and impact strength, excellent performance in terms of dry cutting and polishing stone.